Carbodeon demonstrates NanoDiamond nickel coatings with enhanced tribological properties



New generation of affordable NanoDiamond coatings can reduce wear rate by as much as 85 percent, with Vickers hardness of as much as 1030 Hv after annealing, without increasing surface friction

Helsinki, Finland – 6th June 2017 - Nanodiamond material specialist Carbodeon of Finland has worked with metal finishing specialist CCT Plating of Germany, to develop a new NanoDiamond enhanced electroless nickel plating with significantly improved performance in sliding applications.

Electroless nickel coatings offer many advantages over other coating types, such as excellent corrosion and abrasion resistance, creating an even coating thickness over complex geometries and at relatively low cost. A limitation to their performance has been that they dont perform well in tribological applications involving moving metal parts, where adhesive wear and galling tend to lead to rapid wear or failure.

Incorporating Carbodeon NanoDiamond into the coating solves this problem. Spherical diamond nanoparticles are specially treated to make them disperse in coating liquids and carry a positive electrical charge on their surfaces. In the plating process, the diamond particles behave similarly to positively charged metal ions and together with the coating material they co-deposit onto the component.

Metal-diamond composite surface treatments have already shown their value in abrasion resistant coatings, but in this latest generation of coatings the process has been optimised to better combat adhesive wear, which occurs mainly when the plated parts are in sliding contact with other metal parts.

Key performance characteristics are:
The coating significantly reduces adhesive wear, but does not make the coating abrasive or increase the surface friction.
The coatings can be used as plated which does not affect the substrates heat treatment condition, or can be subjected to annealing for maximum performance.
Wear rate is reduced by 30 percent as plated and by up to 85 percent in the annealed state.
The annealed version has 2 to 3 times the durability of standard annealed coatings.
The coating hardness is significantly increased especially when annealed reaching a maximum Vickers hardness values of 1030 Hv.
The process contains no hexavalent chromium and so is environmentally friendly and free of complex regulations.
Low diamond content makes these coatings affordable.
Target applications include anything which experiences sliding wear, including the automotive, printing, textile manufacturing and oil & gas industries.

The nanomaterial for the process can be obtained from Carbodeon who can also implement the complete plating process in existing customer plating facilities. Alternatively, job plating or turnkey solutions can be carried out by CCT Plating in Stuttgart, Germany.

Carbodeon has patented the nanodiamond material and the plating application.

About Carbodeon
Carbodeon Ltd Oy develops, manufactures and supplies nanodiamond materials for applications where toughness and precision are at a premium. Our many different grades of Ultra-Dispersed NanoDiamonds each possess unique properties fine-tuned for a growing number of dedicated applications. These grades are sold under the name uDiamond. Carbodeon has received major funding from Tekes, European Union and Finnvera. www.carbodeon.com


<